| Name | Chemistry | Grade | Flow Density | Size | Hardness | Application Data |
|
Co1#
Powder
Gas atomized
|
C:2.45 Cr:30.0 Si:1.0 W:13 Ni<3 Fe<3 Mn<1 Mo<1 |
Co1# 711.183 711.153 |
10-15 s 4.3-4.8 g/cm3 |
-180+53micron -53+15micron |
48HRC | HVOF/PTA valve seat inserts,bearing,cutter edge,etc. |
|
Co6#
powder
Gas atomized
|
C:1.2 Cr:29.0 Si:1.0 W:4.5 Ni<3 Fe<3 Mn<1 Mo<1 |
Co6# 716.183 716.153 |
10-15s 4.3-4.8 g/cm3 |
-180+53micron -53+15micron |
38HRC | HVOF/PTA engine valve,high temperature & pressure valve and turbine blade |
|
Co12#
powder
Gas atomized
|
C:1.4 Cr:30.0 Si:1.0 W:8.5 Ni<3 Fe<3 Mn<1 Mo<1 |
Co12# 712.183 712.153 |
10-15s 4.3-4.8 g/cm3 |
-180+53micron -53+15micron |
42HRC | HVOF/PTA high temperature and pressure valves, sawteeth, screw flights, etc. |
|
Co21#
powder
Gas atomized
|
C:0.25 Cr:27.0 Si:1.0 W:0.2 Ni<3 Fe<3 Mn<2 Mo:5.5 |
Co21# 732.183 732.153 |
10-15s 4.3-4.8 g/cm3 |
-180+53micron -53+15micron |
28HRC | HVOF/PTA turbine blades,fluid valve,vlave seat. |
|
Co80#
powder
Gas atomized
|
C:0.08 Cr:18.0 Si:3.4 Ni<1.5 Fe<1.5 Mo:28 |
Co80# 766.183 766.153 |
10-15s 4.3-4.8 g/cm3 |
-180+53micron -53+15micron |
HRC53 | HVOF/PTA wedge gate valves at elevated temperature & corrosive environmnts,plastic extrusion liners |
|
Co190#
powder
Gas atomized
|
C:3.4 Cr:26.5 Si:0.5 Mn<1.5 Mo<1.0 W:14.0 Fe<3.0 |
Co190# | 10-15s 4.3-4.8 g/cm3 |
180+53micron -53+15micron |
HRC55 | HVOF/PTA Oil&gas tool application |
|
PX-Co1
PX-Co6
PX-Co12
PX-Co21
|
Bare rod diameter 3.2-8.0mm ength 1000mm or 2000mm |
TIG/MIG/Fusing welding valve seat/saw blade etc. |
||||
| Co Alloy saw tips |
1,6,12,etc. | Details see attached file of SAW TIPS grade. |