| Name | Chemistry | Grade | Flow Density | Size | Hardness | Application Data |
| NiAl powder clad |
NiAl 95/5 90/10 85/15 |
NiAl | 18-21 s/50g 3.8-4.2 g/cm3 |
90-45um 106-45um |
/ | Self-adhesion bondcoat powder for ceramic and abradable top coatings Exothermic reaction during spraying creates excellent self-bonding coating which is dense and machinable High temperature oxidation and abrasion resistance For salvage and build-up on carbon and corrosion resistant steels Service up to 800°C (1,470 °F) |
| NiCr alloy atomized |
Ni:80 Cr:20 |
NiCr80/20 | 17-21 s/50g 4.2-4.5 g/cm3 |
105-45um -53+15um |
/ | Resists high temp. oxidizing and corrosive gases, prevents scalingon carbon and low alloy steels Good bondcoat for ceramic top coats Higher chromium enhances corrosion resistance Sputtering Target powder itself or as bond coat Service up to 980°C (1,800 °F) |
| Ni/graphite | Ni:85 Graphite:15 |
NiC85/15 | 28-35 s/50g 1.8-2.3 g/cm3 |
90-45um | / | coatings are lubricious and suited for friction applications Flame spraying offers good abradablity, Sacrificial coatings good for clearance control, useful up to 900 F(482 C) |
| Pure Tititanium CPTi powder HDH |
Ti:99.5% | Ti99.5 | 30-40 s/50g 1.4-2.4 g/cm3 |
250-150um 180-75um |
/ | Biocompatibility for medical application; coating with porous structures for implants; corrosion resistant; bond coat for hydroxyapatite. |